Corrosion Resistance Aluminum Round Bar / Rod 6061 T6
Hot Rolled Aluminium Rod 6061 T6
Chemical composition for Hot Rolled Aluminium Rod 6061 T6
| Si | Mn | Cr | Zn | Mg | Ti | Fe | Cu |
| 0.40~0.8 | 0.15max | 0.04~0.35 | 0.25 | 0.8~1.2 | 0.15 | 0.7 | 0.15~0.4 |
1. Aluminum , Grade: 6061, T6 or T651
2. Hot rolled, Temper & Pre-stretching ,,T651
3.Production leadtime: 25~45days
4. Tensile strength: σb (MPa):≥180
Yield strength :σ0.2 (MPa):≥110
Elongation rate: δ5 (%):≥14
Forming
Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.